Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) vs. HexForce® 282 3K Plain Weave Carbon
Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) (Hexcel Corporation) and HexForce® 282 3K Plain Weave Carbon (Hexcel Corp) achieve a 98.3% ASTM engineering compatibility score in Carbon Fiber Fabrics (3K / 6K / 12K), Spread-Tow & Prepregs. Tensile strength delta is +57.9 MPa (+1.5%) and thermal HDT delta is matched, making them qualified for direct drop-in substitution under standard cure schedules.
Side-by-Side ASTM Mechanical, Thermal, Rheological & Pricing Delta
| ASTM Parameter | A: Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) (Hexcel Corporation) | B: HexForce® 282 3K Plain Weave Carbon (Hexcel Corp) | Engineering Delta (A vs. B) |
|---|---|---|---|
| OEM Manufacturer & SKU | Hexcel Corporation • HXL-HF3733-50 | Hexcel Corp • HEX-HF282-3K-50IN | Cross-Brand OEM Equivalent |
| ASTM D638 Tensile Strength (MPa / PSI) | 3850 MPa (558,396 psi) | 3792.1 MPa (550,000 psi) | +57.9 MPa (+1.5 %) |
| ASTM D648 Heat Deflection Temp (HDT °C / °F) | N/A | 260 °C (500 °F) | Ambient / N/A |
| ASTM D790 Flexural Strength (MPa) | 1610 MPa | 5498.5 MPa | -3888.5 MPa (-70.7 %) |
| ASTM D2583 Barcol Hardness | N/A | N/A | N/A |
| ASTM D2196 Brookfield Viscosity @ 25°C | Solid Reinforcement / Core | 198 cPs | Solid State |
| Gel Time @ 25°C (Minutes) | N/A | 35 min | N/A |
| ASTM D792 Specific Density (kg/m³) | 1790 kg/m³ | 1120 kg/m³ | +670 kg/m³ |
| US DOT 49 CFR & TDG Hazmat Class | Non-Regulated Industrial Fiber (N/A) | Non-Hazmat Standard Freight (N/A) | Identical (N/A) |
| Unit Price ($/kg USD) & Pack Price | $46/kg • $2,070 (100 yd Roll (45 kg)) | $14.25/kg • $2,850 (100-Yd Master Roll (50 in)) | +31.75 $/kg (+222.8 %) |
| US Stocking Warehouses | Tacoma, WA • Stamford, CT • Anderson, SC | NC • CA • WA • TX | 1–3 Days LTL Dispatch |
Companion process stack: Low-Viscosity Infusion Epoxy (Gurit Prime 37 / Hexion RIMR 135 / Araldite LY 1564) + Stoichiometric Amine Hardener. Follow SIZE COMPATIBILITY: Use Epoxy-compatible silane sizing with Structural Epoxy Resins (approx. 55:45 fiber-to-resin weight ratio in vacuum infusion). ITAR/EAR export screening applies.
Direct Drop-In Qualified: Thermal deflection (ASTM D648 HDT) differs by only 0 °C (N/A °C vs. 260 °C). Existing mold cure and demold cycles can be maintained without thermal schedule modification.
Identical Hazmat Logistics Profile: Both SKUs ship under US DOT 49 CFR & Transport Canada TDG as Non-Regulated Industrial Fiber (UN Number: N/A). Note 49 CFR § 177.848 segregation if ordering with Class 5.2 Organic Peroxides (UN3105).
Engineering FAQ: Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) vs. HexForce® 282 3K Plain Weave Carbon
1. Is Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) a direct drop-in equivalent for HexForce® 282 3K Plain Weave Carbon?▼
Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) (Hexcel Corporation) and HexForce® 282 3K Plain Weave Carbon (Hexcel Corp) achieve a 98.3% ASTM engineering compatibility score in Carbon Fiber Fabrics (3K / 6K / 12K), Spread-Tow & Prepregs. Tensile strength delta is +57.9 MPa (+1.5%) and thermal HDT delta is matched, making them qualified for direct drop-in substitution under standard cure schedules.
2. What is the ASTM D638 Tensile Strength and ASTM D648 HDT difference between Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) and HexForce® 282 3K Plain Weave Carbon?▼
Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) (Hexcel Corporation) delivers ASTM D638 Tensile Strength of 3850 MPa (558,396 psi) and ASTM D648 HDT of N/A °C, whereas HexForce® 282 3K Plain Weave Carbon (Hexcel Corp) delivers 3792.1 MPa (550,000 psi) and HDT of 260 °C. The net delta is +57.9 MPa (+1.5 %) tensile and N/A HDT.
3. Do Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) and HexForce® 282 3K Plain Weave Carbon use the same catalyst or hardener cure system?▼
Companion process stack: Low-Viscosity Infusion Epoxy (Gurit Prime 37 / Hexion RIMR 135 / Araldite LY 1564) + Stoichiometric Amine Hardener. Follow SIZE COMPATIBILITY: Use Epoxy-compatible silane sizing with Structural Epoxy Resins (approx. 55:45 fiber-to-resin weight ratio in vacuum infusion). ITAR/EAR export screening applies. Direct Drop-In Qualified: Thermal deflection (ASTM D648 HDT) differs by only 0 °C (N/A °C vs. 260 °C). Existing mold cure and demold cycles can be maintained without thermal schedule modification.
4. How do US DOT 49 CFR Hazmat shipping rules and B2B drum/pack prices compare between Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) and HexForce® 282 3K Plain Weave Carbon?▼
Identical Hazmat Logistics Profile: Both SKUs ship under US DOT 49 CFR & Transport Canada TDG as Non-Regulated Industrial Fiber (UN Number: N/A). Note 49 CFR § 177.848 segregation if ordering with Class 5.2 Organic Peroxides (UN3105). In US B2B distribution, Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) is priced at $2,070 per 100 yd Roll (45 kg) ($46/kg) vs. $2,850 per 100-Yd Master Roll (50 in) ($14.25/kg) for HexForce® 282 3K Plain Weave Carbon (delta: +31.75 USD/kg).
Related Drop-In Comparisons in Carbon Fiber Fabrics (3K / 6K / 12K), Spread-Tow & Prepregs
Hexcel HexForce 3733 3K Plain Weave Carbon Fabric (197 gsm) (Hexcel Corporation) and HexForce® 282 3K Plain Weave Carbon (Hexcel Corp) are trademarks of their respective owners. CompositeMatrix Technologies Inc. is an independent North American B2B composite material intelligence registry; comparative ASTM D638, D648, D790, D2583, and D2196 figures are presented under the US legal doctrine of Nominative Fair Use (Lanham Act, 15 U.S.C. § 1125) and Feist Publications, Inc. v. Rural Telephone Service Co. (499 U.S. 340) for scientific and industrial cross-reference. Cure schedules, exotherm behavior, and laminate qualification must be verified by a licensed Naval Architect or Professional Engineer (PE) against current manufacturer batch Technical Data Sheets (TDS) and Safety Data Sheets (SDS).