Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass vs. Vectorply® E-BXM 1708 Biaxial E-Glass
Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass (Vectorply Corporation) and Vectorply® E-BXM 1708 Biaxial E-Glass (Vectorply Corp) achieve a 83.8% ASTM engineering compatibility score in E-Glass / E-CR Stitched Multiaxials (1708 / 1808) & Kevlar Hybrids. Tensile strength delta is -2417.6 MPa (-77.9%) and thermal HDT delta is matched, making them interchangeable with post-cure temperature and viscosity flow adjustments.
Side-by-Side ASTM Mechanical, Thermal, Rheological & Pricing Delta
| ASTM Parameter | A: Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass (Vectorply Corporation) | B: Vectorply® E-BXM 1708 Biaxial E-Glass (Vectorply Corp) | Engineering Delta (A vs. B) |
|---|---|---|---|
| OEM Manufacturer & SKU | Vectorply Corporation • VEC-EBX1200-50 | Vectorply Corp • VEC-1708-50IN-ROLL | Cross-Brand OEM Equivalent |
| ASTM D638 Tensile Strength (MPa / PSI) | 685 MPa (99,351 psi) | 3102.6 MPa (450,000 psi) | -2417.6 MPa (-77.9 %) |
| ASTM D648 Heat Deflection Temp (HDT °C / °F) | N/A | 232.2 °C (450 °F) | Ambient / N/A |
| ASTM D790 Flexural Strength (MPa) | 830 MPa | 4498.8 MPa | -3668.8 MPa (-81.6 %) |
| ASTM D2583 Barcol Hardness | N/A | N/A | N/A |
| ASTM D2196 Brookfield Viscosity @ 25°C | Solid Reinforcement / Core | 805 cPs | Solid State |
| Gel Time @ 25°C (Minutes) | N/A | 35 min | N/A |
| ASTM D792 Specific Density (kg/m³) | 2560 kg/m³ | 1120 kg/m³ | +1440 kg/m³ |
| US DOT 49 CFR & TDG Hazmat Class | Non-Regulated Industrial Fiber (N/A) | Non-Hazmat Standard Freight (N/A) | Identical (N/A) |
| Unit Price ($/kg USD) & Pack Price | $6.35/kg • $635 (100 kg Roll (50 in)) | $1.57/kg • $315 (65-Yd Roll (50 in Width)) | +4.78 $/kg (+304.5 %) |
| US Stocking Warehouses | Phenix City, AL • Tampa, FL • Minneapolis, MN | FL • SC • ME • MN | 1–3 Days LTL Dispatch |
Companion process stack: Marine Vinyl Ester Resin (~0.68 kg/m² per ply in VIP) + Norox MEKP-925H Catalyst (1.5%). Follow RESIN DEMAND FORMULA: 1708 Biaxial (25.5 oz/yd² total) absorbs ~0.95 kg of Vinyl Ester resin per m² per ply in hand layup, or ~0.68 kg/m² per ply under vacuum infusion.
Direct Drop-In Qualified: Thermal deflection (ASTM D648 HDT) differs by only 0 °C (N/A °C vs. 232.2 °C). Existing mold cure and demold cycles can be maintained without thermal schedule modification.
Identical Hazmat Logistics Profile: Both SKUs ship under US DOT 49 CFR & Transport Canada TDG as Non-Regulated Industrial Fiber (UN Number: N/A). Note 49 CFR § 177.848 segregation if ordering with Class 5.2 Organic Peroxides (UN3105).
Engineering FAQ: Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass vs. Vectorply® E-BXM 1708 Biaxial E-Glass
1. Is Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass a direct drop-in equivalent for Vectorply® E-BXM 1708 Biaxial E-Glass?▼
Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass (Vectorply Corporation) and Vectorply® E-BXM 1708 Biaxial E-Glass (Vectorply Corp) achieve a 83.8% ASTM engineering compatibility score in E-Glass / E-CR Stitched Multiaxials (1708 / 1808) & Kevlar Hybrids. Tensile strength delta is -2417.6 MPa (-77.9%) and thermal HDT delta is matched, making them interchangeable with post-cure temperature and viscosity flow adjustments.
2. What is the ASTM D638 Tensile Strength and ASTM D648 HDT difference between Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass and Vectorply® E-BXM 1708 Biaxial E-Glass?▼
Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass (Vectorply Corporation) delivers ASTM D638 Tensile Strength of 685 MPa (99,351 psi) and ASTM D648 HDT of N/A °C, whereas Vectorply® E-BXM 1708 Biaxial E-Glass (Vectorply Corp) delivers 3102.6 MPa (450,000 psi) and HDT of 232.2 °C. The net delta is -2417.6 MPa (-77.9 %) tensile and N/A HDT.
3. Do Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass and Vectorply® E-BXM 1708 Biaxial E-Glass use the same catalyst or hardener cure system?▼
Companion process stack: Marine Vinyl Ester Resin (~0.68 kg/m² per ply in VIP) + Norox MEKP-925H Catalyst (1.5%). Follow RESIN DEMAND FORMULA: 1708 Biaxial (25.5 oz/yd² total) absorbs ~0.95 kg of Vinyl Ester resin per m² per ply in hand layup, or ~0.68 kg/m² per ply under vacuum infusion. Direct Drop-In Qualified: Thermal deflection (ASTM D648 HDT) differs by only 0 °C (N/A °C vs. 232.2 °C). Existing mold cure and demold cycles can be maintained without thermal schedule modification.
4. How do US DOT 49 CFR Hazmat shipping rules and B2B drum/pack prices compare between Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass and Vectorply® E-BXM 1708 Biaxial E-Glass?▼
Identical Hazmat Logistics Profile: Both SKUs ship under US DOT 49 CFR & Transport Canada TDG as Non-Regulated Industrial Fiber (UN Number: N/A). Note 49 CFR § 177.848 segregation if ordering with Class 5.2 Organic Peroxides (UN3105). In US B2B distribution, Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass is priced at $635 per 100 kg Roll (50 in) ($6.35/kg) vs. $315 per 65-Yd Roll (50 in Width) ($1.57/kg) for Vectorply® E-BXM 1708 Biaxial E-Glass (delta: +4.78 USD/kg).
Related Drop-In Comparisons in E-Glass / E-CR Stitched Multiaxials (1708 / 1808) & Kevlar Hybrids
Vectorply E-BX 1200 Stitched (+/-45) Double Bias E-Glass (Vectorply Corporation) and Vectorply® E-BXM 1708 Biaxial E-Glass (Vectorply Corp) are trademarks of their respective owners. CompositeMatrix Technologies Inc. is an independent North American B2B composite material intelligence registry; comparative ASTM D638, D648, D790, D2583, and D2196 figures are presented under the US legal doctrine of Nominative Fair Use (Lanham Act, 15 U.S.C. § 1125) and Feist Publications, Inc. v. Rural Telephone Service Co. (499 U.S. 340) for scientific and industrial cross-reference. Cure schedules, exotherm behavior, and laminate qualification must be verified by a licensed Naval Architect or Professional Engineer (PE) against current manufacturer batch Technical Data Sheets (TDS) and Safety Data Sheets (SDS).